2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection
HomeHome > Products > Heat Shrink > 2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection
2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection

2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection

Material(s) DescriptionWarp material: PolyesterWeft material: Irradiated, modified polyolefinCoating: Modified polyolefi
Basic Info.
Model NO. CL-KSD
Specification 6-100mm
Origin Changzhou
Production Capacity 300000m/Month
Product Description

Material(s) DescriptionWarp material: PolyesterWeft material: Irradiated, modified polyolefinCoating: Modified polyolefinOperating temperature range (3000 hours): -40°C to 125°COperating temperature range (1000 hours): -40°C to 150°CMinimum recovery temperature: 110°C Recommended recovery temperature :150°C to 200°CMaximum storage temperature: 50°C Standard:TL52668 TL52361 D44 1959 GMW14327Testing organization:CTI PONY

Product description (CL-KSD)Inside diameter (mm)
D (min.) expanded as supplied d (max.) recovered after heating
φ6/3-B63
φ8/4-B84
φ10/5-B105
φ12/6-B126
φ16/8-B168
φ20/10-B2010
φ25/12-B2512
φ30/15-B3015
φ35/17.5-B3517.5
φ40/20-B4020
φ50/25-B5025
φ60/30-B6030
φ70/35-B7035
φ80/40-B8040
φ100/50-B10050
B:black
Other specifications can be customized

PropertyTest condition(s)Performance
Thermal ageing168 hrs at 125°CNo deterioration in abrasion resistance at 23°C
24 hrs at 125°CNo deterioration in abrasion resistance at 23°C
FlammabilityMVSS 302Burning rate≤100 mm/min
Low temperature flexibility 4 hours at -40°C,10X diameter mandrel No cracking
Abrasion resistance(1.5N load, 0.3mm radius metal blade,60 cpm,50mm stroke, 144 000 cycles)
Environmental Chamber Temperature: -35°C No wear to underlying rubber hose
Environmental Chamber Temperature: 140ºC
Temperature resistance1) Test temperature 140 ºC, for 500 hours2) Remove the sample and cool it to room temperature..Then place the sample at -35°C for 22 hours.3) Then bend the sample 180 degrees around a cylinder with a radius of 30mmTest temperature 140 ºC, for 500 hours
The protection tube is not damagedStandard: TL52668

2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection


2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection


2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection


2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection


2: 1 Woven Fabric Heat Shrinkable Protective Tubing Used in Cars and Wire Harness Protection